Microstructure evolution of laser surface remelted Zn-2.7 wt.%Cu hyperperitectic alloy

Yunpeng Su, Xin Lin, Sen Yang, Meng Wang, Weidong Huang

科研成果: 期刊稿件文章同行评审

3 引用 (Scopus)

摘要

Laser surface remelting experiments on Zn-2.7 wt.%Cu hyperperitectic alloy were performed by using a 5kW CW CO2 laser at beam scanning velocities ranging between 6 and 1,207 mm/s. With the increase of the growth rate, the microstructures of Zn-2.7 wt.% Cu alloy changed from planar interface to lamellar structures, cellular structures, and finally to high velocity absolute stability (HVAS) planar interface at a growth rate of 349 mm/s. The critical growth rate for the transformation from lamellar structure to cells was about 96 mm/s. Quantitative measurement was preformed to reveal the relationship between the average lamellar spacing and the corresponding growth rate, and the results are in excellent agreement with the prediction of the TMK eutectic model.

源语言英语
页(从-至)4763-4771
页数9
期刊Journal of Materials Science
42
13
DOI
出版状态已出版 - 7月 2007

指纹

探究 'Microstructure evolution of laser surface remelted Zn-2.7 wt.%Cu hyperperitectic alloy' 的科研主题。它们共同构成独一无二的指纹。

引用此