Microstructure and mechanical properties of pure Mg after spiral equal-channel extrusion

Jinghui Li, Fuguo Li, Shan Liang, Zhenyi Huang, Mingya Zhang

科研成果: 期刊稿件文章同行评审

2 引用 (Scopus)

摘要

One of the severe plastic deformation techniques, elliptical cross-sectioned spiral equal-channel extrusion (ECSEE) was successfully applied to the pure Mg processed at 200°C and the microstructure and properties were studied. The observation shows that the grains are refined to 2.1 µm after 2-pass deformation. The proportion of high-angle grain boundary increases to 49.4% after 6-pass. The minimum time of grain boundary rotating 30° is about 0.847 ms, and the maximum time is 2.34 ms. TEM observation illustrates the grain morphology evolves from shear bands to recrystallised grains. There was a significant increase in strength to ∼180 MPa but a decrease in the ductility (∼12%) of pure Mg after 6-pass ECSEE. The refinement mechanism is mainly divided into mechanical and physical refinement.

源语言英语
页(从-至)384-394
页数11
期刊Materials Science and Technology
37
4
DOI
出版状态已出版 - 2021

指纹

探究 'Microstructure and mechanical properties of pure Mg after spiral equal-channel extrusion' 的科研主题。它们共同构成独一无二的指纹。

引用此