Mechanical and electrical properties of lithium stabilized sodium beta alumina solid electrolyte shaping by non-aqueous gelcasting

A novel non-aqueous gelcasting system based on the polymerization of 2-hydroxyethyl methacrylate (HEMA) with low toxicity is applied to the fabrication of lithium stabilized beta alumina solid electrolyte (Li-BASE). Triethanolamine and polyethylene glycol (MW. 1000) are used as dispersant and plasticizer, respectively. Effects of dispersant concentration, solids loading and plasticizer concentration on the rheological behavior of the suspensions are investigated and optimized. Cracking and warpage phenomena in the gelcast green body during drying process are discussed. Green body gelcast from the optimized suspension shows homogeneous microstructure with a relative density of 59.4 % and a bending strength of 17 MPa. Properties, including the relative density, phase composition, microstructure, bending strength and ionic conductivity, of Li-BASEs sintered from green body formed by gelcasting and cold isostatic press are evaluated. Results show that gelcasting forming technique performs well in preparing BASE ceramics with high Weibull modulus and ionic conductivity.