Low-cost preparation and frictional behaviour of a three-dimensional needled carbon/silicon carbide composite

Yanzhi Cai, Yongdong Xu, Bin Li, Shangwu Fan, Litong Zhang, Laifei Cheng, Lin Yu

科研成果: 期刊稿件文章同行评审

41 引用 (Scopus)

摘要

A low-cost carbon/silicon carbide (C/SiC) composite was manufactured by phenolic resin impregnation-pyrolysis combined with liquid silicon infiltration. The carbon fiber preform was prepared by three-dimensional needling. A carbon/carbon composite with a density of 1.22 g/cm3 after only one impregnation-pyrolysis cycle was achieved by using hot-pressing curing. The density of the final C/SiC was 2.10 g/cm3 with a porosity of 4.50% and SiC-content of 45.73%. The C/SiC composite had a high thermal conductivity of 48.72 W/(m K) perpendicular to the friction surface and demonstrated good friction and wear properties. The static and average dynamic friction coefficients were 0.68 and 0.32 (at a braking velocity of 28 m/s). The weight wear rates of the rotating disk and stationary disk were respectively 7.71 and 5.60 mg/cycle with linear wear rates, 1.67 and 1.22 μm/cycle, at a braking velocity of 28 m/s.

源语言英语
页(从-至)497-503
页数7
期刊Journal of the European Ceramic Society
29
3
DOI
出版状态已出版 - 2月 2009

指纹

探究 'Low-cost preparation and frictional behaviour of a three-dimensional needled carbon/silicon carbide composite' 的科研主题。它们共同构成独一无二的指纹。

引用此