Investigation of in-situ microstructural mechanical properties and thermal damage mechanisms of SiCf/SiC under CVI and PIP processes

Lu Zhang, Hongjiao Lin, Zhongyuan Sun, Xiangyu Cai, Tao Feng, Zhixun Wen, Shouyi Sun

科研成果: 期刊稿件文章同行评审

2 引用 (Scopus)

摘要

This study compared the in-situ microstructural mechanical properties of SiCf/SiC composites fabricated by CVI and CVI + PIP process. The investigation revealed that the degree of fiber damage caused by PIP process was 13.8 % before oxidation and 21.9 % after oxidation. TEM was employed to compare the oxidation thickness and element distribution of two processes. The results indicated that external oxygen exhibited longitudinal infiltration oxidation, whereas PIP process introduced oxygen into the material, causing the internal oxygen to diffuse the oxidation process horizontally. As a result of the joint action of internal and external oxygen, the material ultimately exhibited a uniformly oxidized state.

源语言英语
文章编号114689
期刊Materials Characterization
220
DOI
出版状态已出版 - 2月 2025

指纹

探究 'Investigation of in-situ microstructural mechanical properties and thermal damage mechanisms of SiCf/SiC under CVI and PIP processes' 的科研主题。它们共同构成独一无二的指纹。

引用此