Interfacial characteristics and mechanical properties of W fiber reinforced ZrTiCuNiBe amorphous matrix composite

Chunsheng Chen, Jinshan Li, Weifeng Ma, Hongchao Kou, Rui Hu, Lian Zhou, Hengzhi Fu

科研成果: 期刊稿件文章同行评审

4 引用 (Scopus)

摘要

The W fiber reinforced Zr41.25Ti13.75 Cu12.5Ni10Be22.5 amorphous matrix composites with 50 mm in length and 6 mm in diameter have been produced by the melt infiltration casting method. The interface reaction appearance of the composite was analyzed by scanning electron microscopy at the same infiltration time and different infiltration temperatures. The interfacial shear strength of composite is determined by the push-out method. The relations between the macroscopically compressive fracture behaviors with the interfacial characteristics and shear strength are discussed in the end. The results indicate that the plastic behaviors and fracture toughness of amorphous alloy were improved obviously, the interfacial combination of composites included the two processes of interface diffusion and interface reaction, and the interfacial shear strength increased when the interface reaction was pricked up. At the same time, the compressive failure mode of composite changed from the longitudinal split to the single shear failure.

源语言英语
页(从-至)1390-1393
页数4
期刊Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering
36
8
出版状态已出版 - 8月 2007

指纹

探究 'Interfacial characteristics and mechanical properties of W fiber reinforced ZrTiCuNiBe amorphous matrix composite' 的科研主题。它们共同构成独一无二的指纹。

引用此