Influence of graphite on tribological properties of C/SiC braking material from needled felt

Ben Xing Dong, Yong Dong Xu, Yan Zhi Cai, Juan Jiang, Shang Wu Fan, Li Tong Zhang, Lai Fei Cheng

科研成果: 期刊稿件文章同行评审

2 引用 (Scopus)

摘要

Carbon/carbon (C/C) composite with graphite filler addition was prepared by single-direction pressure and pyrolysis, and then a low-cost needle-punched carbon fiber reinforced carbon/silicon carbide (C/SiC) braking material was prepared by reaction melt infiltration. The tribological properties and microstructures of the composite were investigated. The results showed that the graphite mainly existed inside the short-cut webs and between the fiber bundles. The average coefficient of friction (COF) and the friction stability coefficient were rised to the maximum of 0.60, 0.78 at a brake velocity of 10 m/s. The COF curve rised smoothly and stably at high braking speed, and the wear rate as well as the friction surface temperature decreased obviously as the addition of the graphite filler. The friction film which could relieve the direct contact between the friction surfaces was easily formed on the friction surface. As a result, the tribological properties of C/SiC braking material were significantly improved.

源语言英语
页(从-至)51-55
页数5
期刊Hangkong Cailiao Xuebao/Journal of Aeronautical Materials
29
5
出版状态已出版 - 10月 2009

指纹

探究 'Influence of graphite on tribological properties of C/SiC braking material from needled felt' 的科研主题。它们共同构成独一无二的指纹。

引用此