In-situ observations of the tensile deformation and fracture behavior of a fine-grained titanium alloy sheet

Xuehua Zhang; Shuangyin Zhang; Qinyang Zhao; Yongqing Zhao; Rong Li; Weidong Zeng

doi:10.1016/j.jallcom.2018.01.009

In-situ observations of the tensile deformation and fracture behavior of a fine-grained titanium alloy sheet

Xuehua Zhang, Shuangyin Zhang, Qinyang Zhao, Yongqing Zhao, Rong Li, Weidong Zeng

材料学院

科研成果: 期刊稿件 › 文章 › 同行评审

36 引用（Scopus）

摘要

Deformation and crack initiation of industrial Ti-6Al-4V titanium alloy sheet were investigated using in-situ scanning electron microscopy (SEM) at room temperature. The results showed that slip band originated from α/α and α/β interfaces when the tension reaches the yield stage, and the slip mode develops from single slip to multi slip and finally the cross-slip occurs. Microcracks initiate primarily at the phase boundary or along the slip band within α phase, cracks are mainly connected along the 45° line. The fracture surface is full of dimples. Intergranular cracking is the main fracture mechanism.

源语言	英语
页（从-至）	660-668
页数	9
期刊	Journal of Alloys and Compounds
卷	740
DOI	https://doi.org/10.1016/j.jallcom.2018.01.009
出版状态	已出版 - 5 4月 2018

访问文件

10.1016/j.jallcom.2018.01.009

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{48b1c346470140caa9e62de5085a3025,

title = "In-situ observations of the tensile deformation and fracture behavior of a fine-grained titanium alloy sheet",

abstract = "Deformation and crack initiation of industrial Ti-6Al-4V titanium alloy sheet were investigated using in-situ scanning electron microscopy (SEM) at room temperature. The results showed that slip band originated from α/α and α/β interfaces when the tension reaches the yield stage, and the slip mode develops from single slip to multi slip and finally the cross-slip occurs. Microcracks initiate primarily at the phase boundary or along the slip band within α phase, cracks are mainly connected along the 45° line. The fracture surface is full of dimples. Intergranular cracking is the main fracture mechanism.",

keywords = "Fracture surface, In-situ SEM, Slip band, Ti-6Al-4V titanium alloy",

author = "Xuehua Zhang and Shuangyin Zhang and Qinyang Zhao and Yongqing Zhao and Rong Li and Weidong Zeng",

note = "Publisher Copyright: {\textcopyright} 2018 Elsevier B.V.",

year = "2018",

month = apr,

day = "5",

doi = "10.1016/j.jallcom.2018.01.009",

language = "英语",

volume = "740",

pages = "660--668",

journal = "Journal of Alloys and Compounds",

issn = "0925-8388",

publisher = "Elsevier B.V.",

}

TY - JOUR

T1 - In-situ observations of the tensile deformation and fracture behavior of a fine-grained titanium alloy sheet

AU - Zhang, Xuehua

AU - Zhang, Shuangyin

AU - Zhao, Qinyang

AU - Zhao, Yongqing

AU - Li, Rong

AU - Zeng, Weidong

PY - 2018/4/5

Y1 - 2018/4/5

N2 - Deformation and crack initiation of industrial Ti-6Al-4V titanium alloy sheet were investigated using in-situ scanning electron microscopy (SEM) at room temperature. The results showed that slip band originated from α/α and α/β interfaces when the tension reaches the yield stage, and the slip mode develops from single slip to multi slip and finally the cross-slip occurs. Microcracks initiate primarily at the phase boundary or along the slip band within α phase, cracks are mainly connected along the 45° line. The fracture surface is full of dimples. Intergranular cracking is the main fracture mechanism.

AB - Deformation and crack initiation of industrial Ti-6Al-4V titanium alloy sheet were investigated using in-situ scanning electron microscopy (SEM) at room temperature. The results showed that slip band originated from α/α and α/β interfaces when the tension reaches the yield stage, and the slip mode develops from single slip to multi slip and finally the cross-slip occurs. Microcracks initiate primarily at the phase boundary or along the slip band within α phase, cracks are mainly connected along the 45° line. The fracture surface is full of dimples. Intergranular cracking is the main fracture mechanism.

KW - Fracture surface

KW - In-situ SEM

KW - Slip band

KW - Ti-6Al-4V titanium alloy

UR - http://www.scopus.com/inward/record.url?scp=85044374492&partnerID=8YFLogxK

U2 - 10.1016/j.jallcom.2018.01.009

DO - 10.1016/j.jallcom.2018.01.009

M3 - 文章

AN - SCOPUS:85044374492

SN - 0925-8388

VL - 740

SP - 660

EP - 668

JO - Journal of Alloys and Compounds

JF - Journal of Alloys and Compounds

ER -

In-situ observations of the tensile deformation and fracture behavior of a fine-grained titanium alloy sheet

摘要

访问文件

其它文件与链接

指纹

引用此