Imprinted Fe–Ni double hydroxide nanorods with high selective protein adsorption capacity

Ting Wang, Yanting Lyu, Kehan Zhao, Mudasir Ahmad, Baoliang Zhang

科研成果: 期刊稿件文章同行评审

摘要

Anchoring more template proteins on the carrier surface is one of the most critical steps in the preparation process of protein-imprinted polymers. Inspired by the stable interactions between metal ions and proteins, high external surface iron-nickel double hydroxides (Fe–Ni LDH) derived from metal–organic framework were selected as carriers to develop high-performance surface bovine serum albumin (BSA) imprinted iron-nickel double hydroxides nanorods (Fe–Ni LDH@MIP). A hexagonal hollow structure Fe–Ni LDH was synthesized with nanosheets stacked on the surface by etching MIL-88A with Ni2+. The etching of Ni2+ increased the surface roughness of MIL-88A and the rough surface of the carrier was conducive to improving the anchorage amount of BSA, thus providing more effective imprinting sites. Controlled coating of the imprinted polymer layer on the surface of Fe–Ni LDH was obtained by aqueous phase precipitation polymerization. The protein adsorption amount reached 329.8 ± 7.8 mg/g in 60 min with an imprinting factor of 2.86. Fe–Ni LDH@MIP also demonstrated excellent and specific recognition ability in the separation of mixed proteins and fetal bovine serum (FBS) and had good adsorption selectivity, whose adsorption capacity only decreased by 11.5% after 7 adsorption–desorption cycles. In short, Fe–Ni LDH@MIP has great potential to apply in the separation and purification of biomolecules. Graphical abstract: (Figure presented.)

源语言英语
页(从-至)19837-19854
页数18
期刊Journal of Materials Science
59
42
DOI
出版状态已出版 - 11月 2024

指纹

探究 'Imprinted Fe–Ni double hydroxide nanorods with high selective protein adsorption capacity' 的科研主题。它们共同构成独一无二的指纹。

引用此