High-sensitivity X-ray detectors based on solution-grown caesium lead bromide single crystals

Hongjian Zhang, Fangbao Wang, Yufei Lu, Qihao Sun, Yadong Xu, Bin Bin Zhang, Wanqi Jie, Mercouri G. Kanatzidis

科研成果: 期刊稿件文章同行评审

149 引用 (Scopus)

摘要

X-ray detection is of great significance for medical diagnostics, industrial non-destructive inspection, nuclear plants and scientific research. However, high sensitivity is needed for X-ray detectors to reduce the radiation dose applied to human bodies for the applications of medical imaging and security checks. Here, we reported sensitive X-ray detectors made of solution-grown inorganic lead perovskite CsPbBr3 single crystals and the synthesis of high-quality inorganic lead perovskite CsPbBr3 single crystals using an improved low temperature solution method, which exhibited high transmittance, mobility and mobility-lifetime products. By designing the detector in an asymmetric electrode configuration, ion migration was effectively suppressed under a high voltage with a low dark current and an outstanding photoresponse. The optimized detector exhibited high sensitivity of 1256 μC Gy-1 cm-2 for 80 kVp X-ray detection under a relatively low electric field of 20 V mm-1, which was 60 times higher than that of commercially used α-Se detectors. Due to its facile synthesis, low cost, long-term stability, and high detection sensitivity, CsPbBr3 is expected to be an outstanding candidate for commercialized sensitive X-ray detectors.

源语言英语
页(从-至)1248-1256
页数9
期刊Journal of Materials Chemistry C
8
4
DOI
出版状态已出版 - 2020

指纹

探究 'High-sensitivity X-ray detectors based on solution-grown caesium lead bromide single crystals' 的科研主题。它们共同构成独一无二的指纹。

引用此