Heat-treated microstructure and mechanical properties of laser solid forming Ti-6Al-4V alloy

Shuangyin Zhang, Xin Lin, Jing Chen, Weidong Huang

科研成果: 期刊稿件文章同行评审

69 引用 (Scopus)

摘要

The effects of heat treatment on the microstructure and mechanical properties of laser solid forming (LSF) Ti-6Al-4V alloy were investigated. The influences of the temperature and time of solution treatment and aging treatment were analyzed. The results show that the microstructure of LSFed samples consists of Widmanstätten α laths and a little acicular in columnar prior β grains with an average grain width of 300 μm, which grow epitaxially from the substrate along the deposition direction (Z). Solution treatment had an important effect on the width, aspect ratio, and volume fraction of primary and secondary α laths, and aging treatment mainly affects the aspect ratio and volume fraction of primary α laths and the width and volume fraction of secondary α laths. Globular α phase was first observed in LSFed samples when the samples were heat treated with solution treatment (950°C, 8 h/air cooling (AC)) or with solution treatment (950°C, 1 h/AC) and aging treatment (550°C, above 8 h/AC), respectively. The coarsening and globularization mechanisms of α phase in LSFed Ti-6Al-4V alloy during heat treatment were presented. To obtain good integrated mechanical properties for LSFed Ti-6Al-4V alloys, an optimized heat treatment regimen was suggested.

源语言英语
页(从-至)537-544
页数8
期刊Rare Metals
28
6
DOI
出版状态已出版 - 12月 2009

指纹

探究 'Heat-treated microstructure and mechanical properties of laser solid forming Ti-6Al-4V alloy' 的科研主题。它们共同构成独一无二的指纹。

引用此