Fragmentation of α grains accelerated by the growth of β phase in Ti–5Al–2Sn–2Zr–4Mo–4Cr during hot deformation

Jin Zhao Sun, Miao Quan Li, Hong Li

科研成果: 期刊稿件文章同行评审

6 引用 (Scopus)

摘要

The fragmentation of elongated α grains accelerated by the growth of β phase in Ti–5Al–2Sn–2Zr–4Mo–4Cr during hot deformation was examined using electron backscattered diffraction (EBSD) and transmission electron microscopy (TEM). It was determined that boundary splitting resulted in the fragmentation of αE. The kinked sharp α grains, which were formed with help of “civilian” growth of β phase, are necessary structures for the fragmentation of elongated α grains. In addition, the texture results showed an initial deviation from Burgers orientation relationship (OR) in α/β interphase boundaries, indicating that the “civilian” growth of the β phase based on the pre-existing β grain boundaries implied a constant loss of coherency in α/β interphase boundaries, which also accelerated the fragmentation of elongated α grains.

源语言英语
文章编号1700200
期刊Advanced Engineering Materials
20
4
DOI
出版状态已出版 - 4月 2018

指纹

探究 'Fragmentation of α grains accelerated by the growth of β phase in Ti–5Al–2Sn–2Zr–4Mo–4Cr during hot deformation' 的科研主题。它们共同构成独一无二的指纹。

引用此