摘要
Flexural behavior of three dimensional carbon/carbon composites (3DC/C composites) was researched using a three-point bend test, and the influence of density and braided structures on the mechanical properties and fracture modes was analysed. The results show that the density has a great impact on the strength and the modulus, and the fracture modes of 3DC/C composites change from shearing failure to tensile breakage with the increase of densification degree.