Fatigue behaviour and residual strength evolution of 2D C/SiC Z-pinned joints prepared by chemical vapour infiltration

Z-pinned joints prepared by chemical vapour infiltration are widely used in ceramic matrix composite components. Excellent fatigue behaviour is important for structural safety. In this study, 2D C/SiC Z-pinned joints were loaded in axial direction of the pins under static and cyclic loading. Internal damage was monitored in situ by an acoustic emission system. The binding force between pin and hole is relatively strong. Meanwhile, the joints exhibite promising resistance to fatigue. The residual strength increased first with the fatigue cycles then decreased after 10⁵ cycles. Microstructural analysis indicated that full-developed cracks and local stress redistribution resultes in the increase in the strength of the joints. The acoustic emission analysis also provides a supplementary understanding of the damage mechanism. The results show that damage fully develops at the early stage of fatigue. When the specimen is reloaded, less AE events are collected before the fatigue maximum stress.