Fabrication of SiCN-Sc2Si2O7 coatings on C/SiC composites at low temperatures

Jia Liu, Litong Zhang, Juan Yang, Laifei Cheng, Yiguang Wang

科研成果: 期刊稿件文章同行评审

39 引用 (Scopus)

摘要

SiCN-Sc2Si2O7 environmental barrier coatings were fabricated on the surface of C/SiC composites at low temperatures by adding Li2CO3 as sintering aids. With this addition, the fabrication temperature could be lowered about 100-200°C. The shrinkage of the polysilazane-Sc2Si2O7 bars with and without Li2CO3 was tested by dilatometer. The results indicate that the shrinkage speed of the polysilazane-Sc2Si2O7 bar with Li2CO3 is faster than the one without Li2CO3, indicating that the Li2CO3 greatly promotes the sintering of polysilazane-Sc2Si2O7. Water-vapor corrosion behavior of the SiCN-Sc2Si2O7 coated C/SiC composites was carried out at 1250°C. The results reveal that the SiCN-Sc2Si2O7 coatings can effectively protect the C/SiC composites. The corrosion resistance of SiCN-Sc2Si2O7 coatings is not degraded by adding Li2CO3.

源语言英语
页(从-至)705-710
页数6
期刊Journal of the European Ceramic Society
32
3
DOI
出版状态已出版 - 3月 2012

指纹

探究 'Fabrication of SiCN-Sc2Si2O7 coatings on C/SiC composites at low temperatures' 的科研主题。它们共同构成独一无二的指纹。

引用此