Fabrication and texture evolution of hexagonal YMnO₃ nanofibers by electrospinning

Hexagonal YMnO₃ nanofibers were successfully fabricated by sol-gel preparation based on electrospinning. The as-spun fibers dried at 125 °C were round and had a rather uniform diameter around 0.7 μm-2 μm over its length. In order to get pure hexagonal YMnO₃ nanofibers, crystalline structures and microstructures of fibers at various temperatures for 6 h were examined by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The reasonable evaluations for the change of morphology with the increasing temperature were proposed. After being heated at 1100 °C for 6 h, the pure hexagonal YMnO₃ nanofibers were obtained with a reduced diameter ranging from 200 nm to 800 nm and the fibers were homogenous in chemical constitution over its length.