Well-aligned TiO2 /Ti nanotube arrays were fabricated by anodic oxidation, then carbon nanotubes (CNTs) were grown into TiO2 /Ti nanotube arrays to form CNTs/ TiO2 /Ti composite nanostructures by catalytic chemical-vapor deposition for different deposition times. The morphology and quality of samples were assessed by field-emission scanning-electron microscopy and Raman spectroscopy. The field emission (FE) results indicate that the FE properties of CNTs/ TiO2 /Ti composite nanostructures were dramatically improved compared with bare TiO2 /Ti nanotube arrays, and when the growth time of CNTs was 60 min, the composite nanostructures possessed the lowest turn-on field of 1.3 V/μm, the highest emission-current density of 10 mA/cm2 was easily gained at 5.6 V/μm, and there was good FE stability.