Exfoliation corrosion of friction stir welded dissimilar 2024-to-7075 aluminum alloys

P. L. Niu, W. Y. Li, N. Li, Y. X. Xu, D. L. Chen

科研成果: 期刊稿件文章同行评审

79 引用 (Scopus)

摘要

The objective of this study was to identify the effect of base metal (BM) locations on the corrosion behavior of friction stir welded dissimilar 2024-T351 to 7075-T651 aluminum alloys joints in an EXCO solution. Electron backscatter diffraction (EBSD), transmission electron microscopy (TEM) and high resolution TEM (HRTEM) were conducted to characterize the microstructure evolution of the BMs and stir zones (SZs). Scanning electron microscopy (SEM) was employed to observe the appearance of these corroded zones. Results reveal that the corrosion resistance of SZs is similar to that of the BM positioning in the retreating side (RS), and intergranular corrosion (IGC) is prevailing. The fine recrystallized grains in SZs exhibit more drastic IGC than that of BMs. The discontinuously distributed grain boundary precipitates and precipitate-free zones in the SZ of 2024 reduce the IGC damage of SZ.

源语言英语
页(从-至)93-100
页数8
期刊Materials Characterization
147
DOI
出版状态已出版 - 1月 2019

指纹

探究 'Exfoliation corrosion of friction stir welded dissimilar 2024-to-7075 aluminum alloys' 的科研主题。它们共同构成独一无二的指纹。

引用此