Elevated temperature oxidation behavior of the new γ-TiAl alloy

Yuanyuan Luo; Zhengping Xi; Yafeng Lu; Xiaonan Mao; Yi Yang; Weidong Zeng

Elevated temperature oxidation behavior of the new γ-TiAl alloy

Yuanyuan Luo, Zhengping Xi, Yafeng Lu, Xiaonan Mao, Yi Yang, Weidong Zeng

材料学院

科研成果: 期刊稿件 › 文章 › 同行评审

摘要

The oxidation behavior of TiA-3Ta-X(Cr, W) alloy was investigated by thermogravimetric method. Isothermal experiments were carried out from 800°C to 900°C in air. The alloy microstructure and the composition as well as the composition distribution of the oxide scale were analysed by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The results show that the oxidation kinetics obey linearity-parabolic law and the total activation energy is 203 kJ/mol at temperature range of 800~900°C for 0~200 h. The scale thickness increases with the increase of time and temperature. A mixture oxide of protective Al₂O₃, AlTaO₄ and TiO₂ is formed for long time which becomes an important factor increasing the thermal stability of TiAl-3Ta-X (Cr, W).

源语言	英语
页（从-至）	219-223
页数	5
期刊	Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering
卷	43
期	1
出版状态	已出版 - 1月 2014

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{fae64b1164ab48cbb97e529a9167d25d,

title = "Elevated temperature oxidation behavior of the new γ-TiAl alloy",

abstract = "The oxidation behavior of TiA-3Ta-X(Cr, W) alloy was investigated by thermogravimetric method. Isothermal experiments were carried out from 800°C to 900°C in air. The alloy microstructure and the composition as well as the composition distribution of the oxide scale were analysed by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The results show that the oxidation kinetics obey linearity-parabolic law and the total activation energy is 203 kJ/mol at temperature range of 800~900°C for 0~200 h. The scale thickness increases with the increase of time and temperature. A mixture oxide of protective Al2O3, AlTaO4 and TiO2 is formed for long time which becomes an important factor increasing the thermal stability of TiAl-3Ta-X (Cr, W).",

keywords = "Oxidation, Oxide layer, TiAl alloy",

author = "Yuanyuan Luo and Zhengping Xi and Yafeng Lu and Xiaonan Mao and Yi Yang and Weidong Zeng",

year = "2014",

month = jan,

language = "英语",

volume = "43",

pages = "219--223",

journal = "Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering",

issn = "1002-185X",

publisher = "Science Press ",

number = "1",

}

TY - JOUR

T1 - Elevated temperature oxidation behavior of the new γ-TiAl alloy

AU - Luo, Yuanyuan

AU - Xi, Zhengping

AU - Lu, Yafeng

AU - Mao, Xiaonan

AU - Yang, Yi

AU - Zeng, Weidong

PY - 2014/1

Y1 - 2014/1

N2 - The oxidation behavior of TiA-3Ta-X(Cr, W) alloy was investigated by thermogravimetric method. Isothermal experiments were carried out from 800°C to 900°C in air. The alloy microstructure and the composition as well as the composition distribution of the oxide scale were analysed by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The results show that the oxidation kinetics obey linearity-parabolic law and the total activation energy is 203 kJ/mol at temperature range of 800~900°C for 0~200 h. The scale thickness increases with the increase of time and temperature. A mixture oxide of protective Al2O3, AlTaO4 and TiO2 is formed for long time which becomes an important factor increasing the thermal stability of TiAl-3Ta-X (Cr, W).

AB - The oxidation behavior of TiA-3Ta-X(Cr, W) alloy was investigated by thermogravimetric method. Isothermal experiments were carried out from 800°C to 900°C in air. The alloy microstructure and the composition as well as the composition distribution of the oxide scale were analysed by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The results show that the oxidation kinetics obey linearity-parabolic law and the total activation energy is 203 kJ/mol at temperature range of 800~900°C for 0~200 h. The scale thickness increases with the increase of time and temperature. A mixture oxide of protective Al2O3, AlTaO4 and TiO2 is formed for long time which becomes an important factor increasing the thermal stability of TiAl-3Ta-X (Cr, W).

KW - Oxidation

KW - Oxide layer

KW - TiAl alloy

UR - http://www.scopus.com/inward/record.url?scp=84894759493&partnerID=8YFLogxK

M3 - 文章

AN - SCOPUS:84894759493

SN - 1002-185X

VL - 43

SP - 219

EP - 223

JO - Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering

JF - Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering

IS - 1

ER -

Elevated temperature oxidation behavior of the new γ-TiAl alloy

摘要

其它文件与链接

指纹

引用此