Electrical properties of hot press sintered NASICON ceramics

Zhu Dongmei, Xie Zhanglong, Luo Fa, Zhou Wancheng

科研成果: 期刊稿件文章同行评审

4 引用 (Scopus)

摘要

Sodium superionic conductor, NASICON ceramic (Na1+xZr 2SixP3-xOn, x=2), was hot-press sintered under different temperatures and the electrical properties of the obtained different samples were investigated. Results show that the relative density of the ceramics can be improved by hot-press process efficiently and the crystal size of the samples are closely related to sintering temperature. With the increase of sintering temperature, both the density and the crystal size of samples increase obviously, resulting in the increase of ionic conductivity of samples as the sintering temperature. When the sintering temperature reaches 1150°C, the ionic conductivity of sample is as high is 3.6×10-3S/cm, which is obviously higher than that of sample sintered at 1000°C (2.13×10-3S/cm). As the frequency increase, the real parts and the imaginary parts of complex dielectric constants for all the samples decrease in 8.2 GHz∼12.4GHz frequency band. The ceramics obtained at the higher temperature possess the higher dielectric constant.

源语言英语
页(从-至)149-152
页数4
期刊Key Engineering Materials
334-335 I
出版状态已出版 - 2007

指纹

探究 'Electrical properties of hot press sintered NASICON ceramics' 的科研主题。它们共同构成独一无二的指纹。

引用此