Effects of molten salt content and reaction temperature on molten salt preparation of CaNaBi2Nb3O12 powder

Xiaoxia Tian, Feng Gao, Shaobo Qu, Hua Ma, Binke Wang

科研成果: 期刊稿件文章同行评审

5 引用 (Scopus)

摘要

Pure bismuth layer-structured ferroelectric CaNaBi2Nb3O12 ceramic powders with anisotropy were prepared by the molten salt method in molten salt fluxes of NaCI–KCl at 750–900 °C. The effects of salt content and calcination temperature on the microstructure and morphology of CaNaBi2Nb3O12 powder were investigated. The phase and the microstructure of reaction products were detected by X-ray diffraction and scanning electron microscopy. The results show that the particle size of CaNaBi2Nb3O12 powders and the level of anisotropy increase with increasing reaction temperature. The sample dispersion gets better with the increase of molten salt content. The CaNaBi2Nb3O12 powders with good micromorphologies were obtained when the mass ratio of salt to raw materials is 1:1.05, calcined at 800 °C for 1 h. The grain is regularly flake-like, with uniform particle size and single good dispersion.

源语言英语
页(从-至)6189-6193
页数5
期刊Journal of Materials Science: Materials in Electronics
26
8
DOI
出版状态已出版 - 23 8月 2015

指纹

探究 'Effects of molten salt content and reaction temperature on molten salt preparation of CaNaBi2Nb3O12 powder' 的科研主题。它们共同构成独一无二的指纹。

引用此