Effects of heat treatments on aluminum oxide coatings deposited on ni-based alloy

Xiufeng Tang; Fa Luo; Chunhan Hseih; Xiangyu Li

doi:10.1142/S0218625X1550016X

Effects of heat treatments on aluminum oxide coatings deposited on ni-based alloy

Xiufeng Tang, Fa Luo, Chunhan Hseih, Xiangyu Li

材料学院

科研成果: 期刊稿件 › 文章 › 同行评审

1 引用（Scopus）

摘要

Al_xO_y films coated on both Ni-based superalloy and silica substrates were prepared by DC reactive magnetron sputtering. Post-deposition annealing was carried out on those as-deposited films. And then 1 h heat treatments were done on the annealed films at constant temperatures ranging from 600-900°C to simulate the high-temperature application. The Al_xO_y film heated at 600°C exhibited good film property. Bonding strength between the 600°C-heated Al_xO_y film and the Ni-based substrate was about 11.6 MPa.

源语言	英语
文章编号	1550016
期刊	Surface Review and Letters
卷	22
期	1
DOI	https://doi.org/10.1142/S0218625X1550016X
出版状态	已出版 - 25 2月 2015

访问文件

10.1142/S0218625X1550016X

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{7cddc4c33103418a9645081bcb7b5774,

title = "Effects of heat treatments on aluminum oxide coatings deposited on ni-based alloy",

abstract = "AlxOy films coated on both Ni-based superalloy and silica substrates were prepared by DC reactive magnetron sputtering. Post-deposition annealing was carried out on those as-deposited films. And then 1 h heat treatments were done on the annealed films at constant temperatures ranging from 600-900°C to simulate the high-temperature application. The AlxOy film heated at 600°C exhibited good film property. Bonding strength between the 600°C-heated AlxOy film and the Ni-based substrate was about 11.6 MPa.",

keywords = "Aluminum oxide film, bonding strength, heat treatments, Ni-based superalloy",

author = "Xiufeng Tang and Fa Luo and Chunhan Hseih and Xiangyu Li",

note = "Publisher Copyright: {\textcopyright} 2015 World Scientific Publishing Company.",

year = "2015",

month = feb,

day = "25",

doi = "10.1142/S0218625X1550016X",

language = "英语",

volume = "22",

journal = "Surface Review and Letters",

issn = "0218-625X",

publisher = "World Scientific Publishing Co. Pte Ltd",

number = "1",

}

TY - JOUR

T1 - Effects of heat treatments on aluminum oxide coatings deposited on ni-based alloy

AU - Tang, Xiufeng

AU - Luo, Fa

AU - Hseih, Chunhan

AU - Li, Xiangyu

PY - 2015/2/25

Y1 - 2015/2/25

N2 - AlxOy films coated on both Ni-based superalloy and silica substrates were prepared by DC reactive magnetron sputtering. Post-deposition annealing was carried out on those as-deposited films. And then 1 h heat treatments were done on the annealed films at constant temperatures ranging from 600-900°C to simulate the high-temperature application. The AlxOy film heated at 600°C exhibited good film property. Bonding strength between the 600°C-heated AlxOy film and the Ni-based substrate was about 11.6 MPa.

AB - AlxOy films coated on both Ni-based superalloy and silica substrates were prepared by DC reactive magnetron sputtering. Post-deposition annealing was carried out on those as-deposited films. And then 1 h heat treatments were done on the annealed films at constant temperatures ranging from 600-900°C to simulate the high-temperature application. The AlxOy film heated at 600°C exhibited good film property. Bonding strength between the 600°C-heated AlxOy film and the Ni-based substrate was about 11.6 MPa.

KW - Aluminum oxide film

KW - bonding strength

KW - heat treatments

KW - Ni-based superalloy

UR - http://www.scopus.com/inward/record.url?scp=84928473565&partnerID=8YFLogxK

U2 - 10.1142/S0218625X1550016X

DO - 10.1142/S0218625X1550016X

M3 - 文章

AN - SCOPUS:84928473565

SN - 0218-625X

VL - 22

JO - Surface Review and Letters

JF - Surface Review and Letters

IS - 1

M1 - 1550016

ER -

Effects of heat treatments on aluminum oxide coatings deposited on ni-based alloy

摘要

访问文件

其它文件与链接

指纹

引用此