Effects of aging temperature on tensile and fatigue behavior of Sn-3.0Ag-0.5Cu solder joints

科研成果: 期刊稿件文章同行评审

21 引用 (Scopus)

摘要

Thermal aging effects on the tensile and fatigue properties of Sn-3.0Ag-0.5Cu (wt%, SAC305) solder joint are investigated. Three series of experiments were conducted at different temperatures, including uniaxial tension experiments for specimens after aging for 24 and 72 h, and low cycle fatigue experiments for specimens after aging for 72 h. The tensile strength and fatigue life of SAC305 solder joint were analyzed statistically by using a modified Weibull distribution model, which takes the thermal aging effect into account and the results agrees well with the experimental data. The maximum tensile strength after aging for 24 h was obtained by aging at room temperature. After aging for 72 h, the maximum tensile strength and longest fatigue life were obtained by aging at the cryogenic temperature. With elevated aging temperatures, the tensile strength and fatigue life decrease. Microstructure observations on the solder joints reveal that with reducing of aging temperatures, the Ag3Sn phase gradually grows and occupies more volume while Cu6Sn5 phase occupies less volume. The high content of Ag3Sn phase can embrittle the solder joint and dominate the tensile failure.

源语言英语
页(从-至)14884-14892
页数9
期刊Journal of Materials Science: Materials in Electronics
28
19
DOI
出版状态已出版 - 1 10月 2017

指纹

探究 'Effects of aging temperature on tensile and fatigue behavior of Sn-3.0Ag-0.5Cu solder joints' 的科研主题。它们共同构成独一无二的指纹。

引用此