Effect of superficial scratch damage on tension properties of carbon/epoxy plain weave laminates

Miaomiao Duan, Zhufeng Yue, Qianguang Song

科研成果: 期刊稿件文章同行评审

摘要

The effect of scratch damage on the tension properties of carbon fiber plain weave laminates has been studied in detail using digital image correlation (DIC) and acoustic emission (AE). A range of scratch lengths was machined onto different laminates. The bearing capacity of the laminates was then compared with that of unaltered samples. The strain field distributions near the scratches were measured and analyzed as a function of scratch length with DIC. Initiation and propagation of damage were monitored during the tensile tests using AE. Failure sites and morphologies were observed and analyzed. The results show that superficial scratches have little effect on the strength of plain weave laminates when the scratch length is less than 80% of the specimen width. Scratches affect the distribution of strain near the scratch but not far away from the scratch or at the back face of the sample. Not all samples broke from the scratch site but instead broke from the free edge of the sample or close to the gripping region.

源语言英语
文章编号5590448
期刊Advances in Civil Engineering
2021
DOI
出版状态已出版 - 2021

指纹

探究 'Effect of superficial scratch damage on tension properties of carbon/epoxy plain weave laminates' 的科研主题。它们共同构成独一无二的指纹。

引用此