Dip-coating of boron nitride interphase and its effects on mechanical properties of SiCf/SiC composites

Donghai Ding; Wancheng Zhou; Fa Luo; Malin Chen; Dongmei Zhu

doi:10.1016/j.msea.2012.01.118

Dip-coating of boron nitride interphase and its effects on mechanical properties of SiC_f/SiC composites

Donghai Ding, Wancheng Zhou, Fa Luo, Malin Chen, Dongmei Zhu

材料学院

Northwestern Polytechnical University Xian

科研成果: 期刊稿件 › 文章 › 同行评审

47 引用（Scopus）

摘要

Boron nitride (BN) coatings were successfully synthesized on KD-1 SiC fibers by dip-coating in boric acid and urea solution followed by heat treatment at 1000°C in nitrogen. The SEM micrographs indicated that the BN coating is smooth. The XRD and Raman spectrum results showed that the composition of the coatings is h-BN. The effects of BN interphase on the mechanical properties of 2.5D SiC fiber reinforced CVI-SiC matrix (SiC/SiC) composites were investigated. The results show that the flexural strength of SiC_f/SiC composites with and without BN interphase is 170MPa and 60MPa, respectively. And, compared to composites without interphase, the SiC_f/SiC composites with BN interphase exhibit an obvious toughened fracture behavior. It is indicated that dip-coating BN interphase can effectively adjust the interfacial bonding strength and improve the mechanical properties of SiC_f/SiC composites.

源语言	英语
页（从-至）	1-5
页数	5
期刊	Materials Science and Engineering: A
卷	543
DOI	https://doi.org/10.1016/j.msea.2012.01.118
出版状态	已出版 - 1 5月 2012

访问文件

10.1016/j.msea.2012.01.118

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{3cc727b926e4483f835260b84875f216,

title = "Dip-coating of boron nitride interphase and its effects on mechanical properties of SiCf/SiC composites",

abstract = "Boron nitride (BN) coatings were successfully synthesized on KD-1 SiC fibers by dip-coating in boric acid and urea solution followed by heat treatment at 1000°C in nitrogen. The SEM micrographs indicated that the BN coating is smooth. The XRD and Raman spectrum results showed that the composition of the coatings is h-BN. The effects of BN interphase on the mechanical properties of 2.5D SiC fiber reinforced CVI-SiC matrix (SiC/SiC) composites were investigated. The results show that the flexural strength of SiCf/SiC composites with and without BN interphase is 170MPa and 60MPa, respectively. And, compared to composites without interphase, the SiCf/SiC composites with BN interphase exhibit an obvious toughened fracture behavior. It is indicated that dip-coating BN interphase can effectively adjust the interfacial bonding strength and improve the mechanical properties of SiCf/SiC composites.",

keywords = "Ceramics, Composites, Mechanical characterization, X-ray diffraction",

author = "Donghai Ding and Wancheng Zhou and Fa Luo and Malin Chen and Dongmei Zhu",

year = "2012",

month = may,

day = "1",

doi = "10.1016/j.msea.2012.01.118",

language = "英语",

volume = "543",

pages = "1--5",

journal = "Materials Science and Engineering: A",

issn = "0921-5093",

publisher = "Elsevier Ltd",

}

TY - JOUR

T1 - Dip-coating of boron nitride interphase and its effects on mechanical properties of SiCf/SiC composites

AU - Ding, Donghai

AU - Zhou, Wancheng

AU - Luo, Fa

AU - Chen, Malin

AU - Zhu, Dongmei

PY - 2012/5/1

Y1 - 2012/5/1

N2 - Boron nitride (BN) coatings were successfully synthesized on KD-1 SiC fibers by dip-coating in boric acid and urea solution followed by heat treatment at 1000°C in nitrogen. The SEM micrographs indicated that the BN coating is smooth. The XRD and Raman spectrum results showed that the composition of the coatings is h-BN. The effects of BN interphase on the mechanical properties of 2.5D SiC fiber reinforced CVI-SiC matrix (SiC/SiC) composites were investigated. The results show that the flexural strength of SiCf/SiC composites with and without BN interphase is 170MPa and 60MPa, respectively. And, compared to composites without interphase, the SiCf/SiC composites with BN interphase exhibit an obvious toughened fracture behavior. It is indicated that dip-coating BN interphase can effectively adjust the interfacial bonding strength and improve the mechanical properties of SiCf/SiC composites.

AB - Boron nitride (BN) coatings were successfully synthesized on KD-1 SiC fibers by dip-coating in boric acid and urea solution followed by heat treatment at 1000°C in nitrogen. The SEM micrographs indicated that the BN coating is smooth. The XRD and Raman spectrum results showed that the composition of the coatings is h-BN. The effects of BN interphase on the mechanical properties of 2.5D SiC fiber reinforced CVI-SiC matrix (SiC/SiC) composites were investigated. The results show that the flexural strength of SiCf/SiC composites with and without BN interphase is 170MPa and 60MPa, respectively. And, compared to composites without interphase, the SiCf/SiC composites with BN interphase exhibit an obvious toughened fracture behavior. It is indicated that dip-coating BN interphase can effectively adjust the interfacial bonding strength and improve the mechanical properties of SiCf/SiC composites.

KW - Ceramics

KW - Composites

KW - Mechanical characterization

KW - X-ray diffraction

UR - http://www.scopus.com/inward/record.url?scp=84862810863&partnerID=8YFLogxK

U2 - 10.1016/j.msea.2012.01.118

DO - 10.1016/j.msea.2012.01.118

M3 - 文章

AN - SCOPUS:84862810863

SN - 0921-5093

VL - 543

SP - 1

EP - 5

JO - Materials Science and Engineering: A

JF - Materials Science and Engineering: A

ER -

Dip-coating of boron nitride interphase and its effects on mechanical properties of SiCf/SiC composites

摘要

访问文件

其它文件与链接

指纹

引用此

Dip-coating of boron nitride interphase and its effects on mechanical properties of SiC_f/SiC composites