Diffusion barrier effect of Al2O3 layer at the interface between Mo-Si-B coating and Nb-Si based alloy

Yanqiang Qiao, Tao Chen, Xiping Guo

科研成果: 期刊稿件文章同行评审

15 引用 (Scopus)

摘要

An oxidation-resistant composite coating, including Mo-Si-B layer and Al2O3 diffusion barrier, was prepared on Nb-Si-based alloy by a two-step method. The Al2O3 film was fabricated by firstly deposition of Al on the alloy through pack cementation, and then by in situ oxidation of the aluminide coating. Mo-Si-B coating was then prepared on the Al2O3 film by spark plasma sintering. The Mo-Si-B coating is mainly composed of MoSi2 and a small amount of MoB and SiO2 particles. After long-term exposure at 1250 °C, the growth of the interdiffusion zone (IDZ) was suppressed effectively at the interface with the Al2O3 diffusion barrier. The results indicate that the diffusion barrier can significantly inhibit the outward diffusion of Nb, Ti and Cr alloying elements as well as the sluggish inward consumption of Si element. The Mo-Si-B coating with Al2O3 diffusion barrier exhibited a good oxidation resistance with a mass gain of about 0.97 mg/cm2 after 500 h of oxidation.

源语言英语
页(从-至)45-56
页数12
期刊Corrosion Communications
4
DOI
出版状态已出版 - 12月 2021

指纹

探究 'Diffusion barrier effect of Al2O3 layer at the interface between Mo-Si-B coating and Nb-Si based alloy' 的科研主题。它们共同构成独一无二的指纹。

引用此