Determination of the enthalpy of fusion and thermal diffusivity for ternary Cu60-xSnxSb40 alloys

W. Zhai, K. Zhou, L. Hu, B. Wei

科研成果: 期刊稿件文章同行评审

6 引用 (Scopus)

摘要

The liquidus and solidus temperatures, enthalpy of fusion, and the temperature dependence of thermal diffusivity for ternary Cu60-xSnxSb40 alloys were systematically measured by DSC and laser flash methods. It is found that both the liquidus temperature and the enthalpy of fusion decrease with the rise of Sn content, and their relationships with alloy composition were established by polynomial functions. The thermal diffusivity usually drops from the solid toward the semi-solid state. The undercoolability of those liquid Cu60-xSnxSb40 alloys with primary Cu2Sb solid phase is stronger than the others with primary β(SnSb) intermetallic compound, and the increase of cooling rate facilitates further undercooling. Microstructural observation indicates that both of the primary Cu2Sb and β(SnSb) intermetallic compounds in ternary Cu60-xSnxSb40 alloys grow in faceted mode, and develop into coarse flakes and polygonal blocks.

源语言英语
页(从-至)159-163
页数5
期刊Journal of Chemical Thermodynamics
95
DOI
出版状态已出版 - 1 4月 2016

指纹

探究 'Determination of the enthalpy of fusion and thermal diffusivity for ternary Cu60-xSnxSb40 alloys' 的科研主题。它们共同构成独一无二的指纹。

引用此