Design of an inlaid interface structure to improve the oxidation protective ability of SiC-MoSi2-ZrB2 coating for C/C composites

Qian Gang Fu; Jun Yi Jing; He Jun Li; Xiu Xiu Jin; Lei Zhuang; Lu Li

doi:10.1016/j.ceramint.2015.11.095

Design of an inlaid interface structure to improve the oxidation protective ability of SiC-MoSi₂-ZrB₂ coating for C/C composites

Qian Gang Fu, Jun Yi Jing, He Jun Li, Xiu Xiu Jin, Lei Zhuang, Lu Li

材料学院

Northwestern Polytechnical University Xian

科研成果: 期刊稿件 › 文章 › 同行评审

24 引用（Scopus）

摘要

To improve the oxidation protective ability of SiC-MoSi₂-ZrB₂ coating for carbon/carbon (C/C) composites, pre-oxidation treatment and pack cementation were applied to construct a buffer interface layer between C/C substrate and SiC-MoSi₂-ZrB₂ coating. The tensile strength increased from 2.29 to 3.35 MPa after pre-oxidation treatment, and the mass loss was only 1.91% after oxidation at 1500 °C for 30 h. Compared with the coated C/C composites without pre-oxidation treatment, after 18 thermal cycles from 1500 °C and room temperature, the mass loss was decreased by 30.6%. The improvements of oxidation resistance and mechanical property are primarily attributed to the formation of inlaid interface between the C/C substrate and SiC-MoSi₂-ZrB₂ coating.

源语言	英语
页（从-至）	4212-4220
页数	9
期刊	Ceramics International
卷	42
期	3
DOI	https://doi.org/10.1016/j.ceramint.2015.11.095
出版状态	已出版 - 15 2月 2016

访问文件

10.1016/j.ceramint.2015.11.095

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{786cd6767a054711aa3c96df980c858d,

title = "Design of an inlaid interface structure to improve the oxidation protective ability of SiC-MoSi2-ZrB2 coating for C/C composites",

abstract = "To improve the oxidation protective ability of SiC-MoSi2-ZrB2 coating for carbon/carbon (C/C) composites, pre-oxidation treatment and pack cementation were applied to construct a buffer interface layer between C/C substrate and SiC-MoSi2-ZrB2 coating. The tensile strength increased from 2.29 to 3.35 MPa after pre-oxidation treatment, and the mass loss was only 1.91% after oxidation at 1500 °C for 30 h. Compared with the coated C/C composites without pre-oxidation treatment, after 18 thermal cycles from 1500 °C and room temperature, the mass loss was decreased by 30.6%. The improvements of oxidation resistance and mechanical property are primarily attributed to the formation of inlaid interface between the C/C substrate and SiC-MoSi2-ZrB2 coating.",

keywords = "C. Thermal shock resistance, Carbon/carbon composites, Oxidation resistance, SiC-MoSi-ZrB coating, Surface treatment",

author = "Fu, {Qian Gang} and Jing, {Jun Yi} and Li, {He Jun} and Jin, {Xiu Xiu} and Lei Zhuang and Lu Li",

note = "Publisher Copyright: {\textcopyright} 2015 Elsevier Ltd and Techna Group S.r.l.",

year = "2016",

month = feb,

day = "15",

doi = "10.1016/j.ceramint.2015.11.095",

language = "英语",

volume = "42",

pages = "4212--4220",

journal = "Ceramics International",

issn = "0272-8842",

publisher = "Elsevier Ltd",

number = "3",

}

TY - JOUR

T1 - Design of an inlaid interface structure to improve the oxidation protective ability of SiC-MoSi2-ZrB2 coating for C/C composites

AU - Fu, Qian Gang

AU - Jing, Jun Yi

AU - Li, He Jun

AU - Jin, Xiu Xiu

AU - Zhuang, Lei

AU - Li, Lu

PY - 2016/2/15

Y1 - 2016/2/15

N2 - To improve the oxidation protective ability of SiC-MoSi2-ZrB2 coating for carbon/carbon (C/C) composites, pre-oxidation treatment and pack cementation were applied to construct a buffer interface layer between C/C substrate and SiC-MoSi2-ZrB2 coating. The tensile strength increased from 2.29 to 3.35 MPa after pre-oxidation treatment, and the mass loss was only 1.91% after oxidation at 1500 °C for 30 h. Compared with the coated C/C composites without pre-oxidation treatment, after 18 thermal cycles from 1500 °C and room temperature, the mass loss was decreased by 30.6%. The improvements of oxidation resistance and mechanical property are primarily attributed to the formation of inlaid interface between the C/C substrate and SiC-MoSi2-ZrB2 coating.

AB - To improve the oxidation protective ability of SiC-MoSi2-ZrB2 coating for carbon/carbon (C/C) composites, pre-oxidation treatment and pack cementation were applied to construct a buffer interface layer between C/C substrate and SiC-MoSi2-ZrB2 coating. The tensile strength increased from 2.29 to 3.35 MPa after pre-oxidation treatment, and the mass loss was only 1.91% after oxidation at 1500 °C for 30 h. Compared with the coated C/C composites without pre-oxidation treatment, after 18 thermal cycles from 1500 °C and room temperature, the mass loss was decreased by 30.6%. The improvements of oxidation resistance and mechanical property are primarily attributed to the formation of inlaid interface between the C/C substrate and SiC-MoSi2-ZrB2 coating.

KW - C. Thermal shock resistance

KW - Carbon/carbon composites

KW - Oxidation resistance

KW - SiC-MoSi-ZrB coating

KW - Surface treatment

UR - http://www.scopus.com/inward/record.url?scp=84951930913&partnerID=8YFLogxK

U2 - 10.1016/j.ceramint.2015.11.095

DO - 10.1016/j.ceramint.2015.11.095

M3 - 文章

AN - SCOPUS:84951930913

SN - 0272-8842

VL - 42

SP - 4212

EP - 4220

JO - Ceramics International

JF - Ceramics International

IS - 3

ER -

Design of an inlaid interface structure to improve the oxidation protective ability of SiC-MoSi2-ZrB2 coating for C/C composites

摘要

访问文件

其它文件与链接

指纹

引用此

Design of an inlaid interface structure to improve the oxidation protective ability of SiC-MoSi₂-ZrB₂ coating for C/C composites