Design and optimization of oxidation resistant coating for C/C aircraft brake materials

Shangwu Fan, Xu Ma, Zuo Li, Jing Hu, Zan Xie, Juanli Deng, Litong Zhang, Laifei Cheng

科研成果: 期刊稿件文章同行评审

28 引用 (Scopus)

摘要

A SiCN/borosilicate glass anti-oxidation coating with double-layer structure was designed for C/C aircraft brake materials. The SiCN layer was introduced as transition layer to improve the wettability between borosilicate glass and C/C composites, and the microstructure results indicated that the coating with SiCN inner layer was dense and uniform. The oxidation resistance evaluation of the coated samples was conducted at 800 °C in air for 10 h. The weight loss of SiCN/borosilicate glass coated samples valued ~ 5.66% indicated that the oxidation resistant property of the simple SiCN/borosilicate glass coating was not good, which was mainly due to the relative large viscosity of borosilicate glass at 800 °C. B4C was introduced to add into the outer glass coating to improve the self-healing ability of the coating. After oxidized at 800 °C in air for 10 h, the weight loss of the SiCN/borosilicate glass-B4C coated samples was ~ 2.48%. B4C could consume the oxygen diffused into the coating and the reacted product B2O3 with a better fluidity at 800 °C could effectively heal cracks and pores in the coating to improve the oxidation resistance property. The reaction of B4C oxidized to B2O3 was accompanied with ~ 1.5 times volume expansion, which was also beneficial for the healing of defects.

源语言英语
页(从-至)175-182
页数8
期刊Ceramics International
44
1
DOI
出版状态已出版 - 1月 2018

指纹

探究 'Design and optimization of oxidation resistant coating for C/C aircraft brake materials' 的科研主题。它们共同构成独一无二的指纹。

引用此