Crystal orientation dependence of Young's modulus in Ti-Nb-based β-titanium alloy

Wenfang Cui, Aihong Guo, Lian Zhou, Chunming Liu

科研成果: 期刊稿件文章同行评审

16 引用 (Scopus)

摘要

The paper investigated the texture evolution of a biomedical β-titanium alloy (Ti-28Nb-13Zr-2Fe) under 15%-85% cold rolling reduction and 700°C-900°C recrystallization annealing treatment, and clarified the effects of crystal orientation on Young's modulus of the alloy. Orientation distribution function (ODF) maps and electron backscatter diffraction (EBSD) analysis revealed that the rolling texture type changed with the increase of reduction according to the sequence: α-fiber texture→γ-fiber texture→α-rotated cubic texture. Young's modulus exhibited the lowest value 54 GPa under 15% reduction. Strong {111}〈112〉 γ-fiber texture was developed after rolling 85% reduction and annealing at 700°C, which was favorable to decreasing Young's modulus in comparison with randomly orientated microstructure. Cyclic loading-unloading tensile test proved that the gradual rotation of {110} slip plane during plastic deformation promoted the development of {001}〈110〉 texture component, leading to the marked decrease of Young's modulus.

源语言英语
页(从-至)1513-1519
页数7
期刊Science China Technological Sciences
53
6
DOI
出版状态已出版 - 6月 2010
已对外发布

指纹

探究 'Crystal orientation dependence of Young's modulus in Ti-Nb-based β-titanium alloy' 的科研主题。它们共同构成独一无二的指纹。

引用此