Characterization of surface layer in TC17 alloy treated by air blast shot peening

Y. G. Liu, H. M. Li, M. Q. Li

科研成果: 期刊稿件文章同行评审

92 引用 (Scopus)

摘要

The air blast shot peening of TC17 alloy was carried out at the air pressures ranges from 0.15. MPa to 0.35. MPa and processing durations ranges from 5. min to 60. min. The effects of the air pressure and processing duration on the microstructure and surface roughness of TC17 alloy were investigated. The experimental results showed that the microstructure gradually changed from nanocrystalline structure in the surface layer to the undeformed grains in the base TC17 alloy. The nanostructured surface layer with equiaxed grains and smallest grain size of 6.7. nm was fabricated in base TC17 alloy. The grain size of nanostructured surface layer in the TC17 alloy decreased with an increase in the air pressure and processing duration. Meanwhile, the results indicated an increasing surface roughness and a decreasing mass of the TC17 alloy specimens with an increase in the air pressure and processing duration due to the air blast shot peening treatment.

源语言英语
页(从-至)120-126
页数7
期刊Materials and Design
65
DOI
出版状态已出版 - 1 1月 2015

指纹

探究 'Characterization of surface layer in TC17 alloy treated by air blast shot peening' 的科研主题。它们共同构成独一无二的指纹。

引用此