Characterization and the improved Arrhenius model of 0Cr11Ni2MoVNb steel during hot deformation process

Jia Fu, Fuguo Li, Yongtang Li

科研成果: 期刊稿件会议文章同行评审

5 引用 (Scopus)

摘要

True stress versus true strain curves of 0Cr11Ni2MoVNb alloy steel were obtained from isothermal compression tests on Gleeble-1500 tester over a wide temperature range from 1223K to 1433K and a strain rate range from 0.01s-1 to 10s-1. Considering the compensation of strain, the improved Arrhenius model based on Zener-Holloman parameter was evaluated by regression analysis and modified by optimizing parameters of strain hardening exponent as well as the deformation activation energy with a method of five-order polynomial fitting. Then constitutive equation of the flow stress was verified by comparing both the correlation coefficient R and the average absolute relative error (AARE). The main result shows that: (1) the deformation activation energy is insensitive to strain rate under a lower temperature range from 1223K to 1373K; (2) maximum values of the deformation activation energy under various strain degree are concentrated with the temperature over 1373K and the strain rate nearby 0.1s-1. (3) the improved Arrhenius model has a low value level of its parameters R(<0.977%) and AARE (<5.031%), which has a good agreement with the experimental values to predict the flow stress at different temperatures and strain rates.

源语言英语
文章编号022027
期刊IOP Conference Series: Materials Science and Engineering
382
2
DOI
出版状态已出版 - 13 7月 2018
活动2018 International Conference on Advanced Materials, Intelligent Manufacturing and Automation, AMIMA 2018 - , 中国
期限: 23 5月 201826 5月 2018

指纹

探究 'Characterization and the improved Arrhenius model of 0Cr11Ni2MoVNb steel during hot deformation process' 的科研主题。它们共同构成独一无二的指纹。

引用此