Surface defect passivation of Ta3N5photoanode via pyridine grafting for enhanced photoelectrochemical performance

Fan Li, Jie Jian, Youxun Xu, Wei Liu, Qian Ye, Fan Feng, Can Li, Lichao Jia, Hongqiang Wang

Research output: Contribution to journalArticlepeer-review

12 Scopus citations

Abstract

Tantalum nitride (Ta3N5) is a promising photoanode material for photoelectrochemical (PEC) water splitting, while the Ta3N5/Ta photoanode synthesized via general thermal oxidation and nitridation on a Ta foil method usually has serious carrier recombination at the surface, which usually reduces the PEC activities. Herein, we demonstrate an efficient strategy of decorating pyridine, a small organic molecule at the surface of the Ta3N5/Ta photoanode, to alleviate the surface recombination. Such decoration yields a stable photocurrent density of 4.4 mA cm-2 at 1.23 VRHE under AM 1.5G (air mass 1.5 global, 100 mW cm-2) simulated sunlight, which is about 1.4 times higher than that of Ta3N5/Ta without modification, and the photocurrent density still remained ∼100% of its original value after a 5 h stability test. Further characterization of the incident photon-to-current conversion efficiency and absorbed photon-to-current efficiency of the pyridine/Ta3N5/Ta photoanode showed a significant increase to 62% and 72% at 500 nm, respectively. The enhanced pyridine/Ta3N5/Ta PEC performance can be attributed to minimizing the density of nitrogen vacancies due to the passivation of pyridine grafting, which results in the decreased recombination centers and improved charge separation efficiency at the surface. We thus believe that our study of surface passivation by using small organic molecules provides an alternative to address the surface recombination of Ta3N5 based photoelectrodes.

Original languageEnglish
Article number024705
JournalJournal of Chemical Physics
Volume153
Issue number2
DOIs
StatePublished - 14 Jul 2020

Fingerprint

Dive into the research topics of 'Surface defect passivation of Ta3N5photoanode via pyridine grafting for enhanced photoelectrochemical performance'. Together they form a unique fingerprint.

Cite this