Abstract
The objective of the present study is to investigate the effect of energy-input on the mechanical properties of a 304 stainless-steel joint welded by continuous-drive rotary friction-welding (RFW). RFW experiments were conducted over a wide range of welding parameters (welding pressure: 25–200 MPa, rotation speed: 500–2300 rpm, welding time: 4–20 s, and forging pressure: 100–200 MPa). The results show that the energy-input has a significant effect on the tensile strength of RFW joints. With the increase of energy-input, the tensile strength rapidly increases until reaching the maximum value and then slightly decreases. An empirical model for energy-input was established based on RFW experiments that cover a wide range of welding parameters. The accuracy of the model was verified by extra RFW experiments. In addition, the model for optimal energy-input of different forging pressures was obtained. To verify the accuracy of the model, the optimal energy-input of a 170 MPa forging pressure was calculated. Three RFW experiments in which energy-input was equal to the calculated value were made. The joints’ tensile strength coefficients were 90%, 93%, and 96% respectively, which proved that the model is accurate.
Original language | English |
---|---|
Article number | 908 |
Journal | Metals |
Volume | 8 |
Issue number | 11 |
DOIs | |
State | Published - 5 Nov 2018 |
Keywords
- Energy-input
- Joint mechanical properties
- Rotary friction-welding