Structure and dielectric properties of Cu and (K,Na) doped SrBi ₂Nb₂O₉ ferroelectric ceramics

Ferroelectric ceramics, SrBi₂Nb₂O₉ (SBN), Sr_0.8Cu_0.2Bi₂Nb₂O₉ (SCBN) and Sr_0.8K_0.1Na_0.1Bi₂Nb ₂O₉ (SKNBN) were prepared by a solid state reaction process. X-ray diffraction analysis shows that the alkali and Cu almost diffuse into the SBN lattice to form a solid solution during sintering and some slight secondary phases was detected. The effect of alkali and Cu on dielectric properties of the SBN ceramics was discussed. The dielectric loss factor of (K,Na) doped SBN ceramics degraded considerably to 0.01 and their frequency and temperature stabilities were enhanced. The dielectric constant was enhanced by approximately 60% and the Curie temperature (Tc) was also improved for Cu doped SrBi₂Nb₂O₉ ceramics.