Abstract
The effects of the ratio of SiO2 and B2O3, the type of addition with high melting point including MoSi2, Y2O3, SiC on the high temperature stability and fluidity of the borosilicate glass coating were studied. Borosilicate glass coating with good high temperature stability and fluidity was prepared on the surface of SiC coated carbon-carbon (C/C) composites. The isothermal oxidation resistance of SiC/borosilicate glass coated C/C composites was also tested under 1500°C in air. The study results showed that the borosilicate glass exhibits good high temperature stability and fluidity as the ratio of SiO2 and B2O3 was 4: 1. The addition of MoSi2 can improve the oxidation resistance of borosilicate coating, and the better oxidation resistance borosilicate glass coating can be obtained as the mass ratio of borosilicate glass and MoSi2 was 4: 1. The mass loss of the SiC/borosilicate glass coated C/C composites was only 4.31% after oxidation for 17 h.
| Original language | English |
|---|---|
| Pages (from-to) | 78-81+86 |
| Journal | Cailiao Gongcheng/Journal of Materials Engineering |
| Issue number | 7 |
| State | Published - Jul 2010 |
Keywords
- Borosilicate glass
- Carbon-carbon (C/C) composite
- Coating
- Oxidation resistance