T1 - Properties and microstructures of melt-processed (YHo)Ba2Cu 3O7-y superconductor
AU - Feng Yong, Yong
AU - Zhou Lian, Lian
AU - Zhang Pingxiang, Pingxiang
AU - Wang Keguang, Keguang
AU - Ji Ping, Ping
AU - Wu Xiaozu, Xiaozu
AU - Luo Changxun, Changxun
AU - Xing Mianrong, Mianrong
PY - 1992
Y1 - 1992
N2 - The authors have prepared (YHo)Ba2Cu3O7-y superconductors with high Jc by the powder melting process (PMP) method. The DTA result shows that the melting temperature of Y-system superconductor can be reduced by Ho addition. The Jc value can be improved and the size of the 211 phase can be reduced by Ho substitution. Microstructures and the X-ray diffraction pattern indicate that the 123 grains are preferentially aligned with mutually parallel a-b conductive planes. There are many twins and fine 211 particles in the sample. Many crystal defects are also found to exist around the 211 phase. These defects may be acting as pinning centres.
AB - The authors have prepared (YHo)Ba2Cu3O7-y superconductors with high Jc by the powder melting process (PMP) method. The DTA result shows that the melting temperature of Y-system superconductor can be reduced by Ho addition. The Jc value can be improved and the size of the 211 phase can be reduced by Ho substitution. Microstructures and the X-ray diffraction pattern indicate that the 123 grains are preferentially aligned with mutually parallel a-b conductive planes. There are many twins and fine 211 particles in the sample. Many crystal defects are also found to exist around the 211 phase. These defects may be acting as pinning centres.
UR - http://www.scopus.com/inward/record.url?scp=0010599467&partnerID=8YFLogxK
U2 - 10.1088/0953-2048/5/7/004
DO - 10.1088/0953-2048/5/7/004
M3 - 文章
AN - SCOPUS:0010599467
SN - 0953-2048
VL - 5
SP - 431
EP - 434
JO - Superconductor Science and Technology
JF - Superconductor Science and Technology
IS - 7
M1 - 004
ER -