Preparation, and magnetic and electromagnetic properties of La-doped strontium ferrite films

SrLa_xFe_12-xO₁₉ films (x=01.0) with large magneto-crystalline anisotropy were synthesized on SiO₂ substrate by solgel and self-propagating high-temperature synthesis technique. The films were characterized by various experimental techniques including X-ray diffraction analysis, Field Emission Scanning Electron Microscope, Atomic Force Microscopy, Vibrating Sample Magnetometry and vector network analyzer. The results show that La ions completely enter into strontium ferrite lattice without changing the ferrite appearance; its grain size is approximately 4080 nm, its length is 100 nm; the magnetoplumbite structure is proved through testing a concertina form of the crystal grain; the maximum coercivity is 5986 Oe at x=0.2; La-doped films possess a wider microwave absorption frequency range with better gross loss angle tangent (tan δ>0.1), from 9 to 10.5 GHz at x=0.2, where the maximum value of tan δ reaches 0.2709. The La-doped films reach smaller nanometer size, better magnetic properties and microwave absorption properties with the doping of lanthanum.