Abstract
Liquid infiltration joining of C/SiC composite with various woven style and Nb was studied. The join procedure was carried out at the temperature of 1300°C with the holding time of 45 min in vacuum. The pressure applied was 20 MPa. Ni-base interlinker was employed as the interlayer. Results showed joints of laminated C/SiC composite and Nb had been disjoined during the joints were cooled from the joining temperature to room temperature. However favorable joints of 3D C/SiC composite and Nb could be gained.