Effects of heat treatment on mechanical properties of 3D Si₃N_4f/BN/Si₃N₄ composites by PIP

The fabrication of three-dimensional silicon nitride (Si₃N₄) fiber-reinforced silicon nitride matrix (3D Si₃N_4f/BN/Si₃N₄) composites with a boron nitride (BN) interphase through precursor infiltration and pyrolysis (PIP) process was reported. Heat treatment at 1000–1200 °C was used to analyze the thermal stability of the Si₃N_4f/BN/Si₃N₄ composites. It was found after heat treatment the flexural strength and fracture toughness change with a pattern that decrease first and then increase, which are 191 ± 13 MPa and 5.8 ± 0.5 MPa·m^1/2 respectively for as-fabricated composites, and reach the minimum values of 138 ± 6 MPa and 3.9 ± 0.4 MPa·m^1/2 respectively for composites annealed at 1100 °C. The influence mechanisms of the heat treatment on the Si₃N_4f/BN/Si₃N₄ composites include: (Ⅰ) matrix shrinkage by further ceramization that causes defects such as pores and cracks in composites, and (Ⅱ) prestress relaxation, thermal residual stress (TRS) redistribution and a better wetting at the fiber/matrix (F/M) surface that increase the interfacial bonding strength (IBS). Thus, heat treatment affects the mechanical properties of composites by changing the properties of the matrix and IBS, where the load transfer efficiency onto the fibers is fluctuating by the microstructural evolution of matrix and gradually increasing IBS.