Effect of orientation on the microstructure of nickel-based crystalline superalloys

X. B. Zhao, L. Liu, S. F. Gao, B. M. Ge, J. Zhang, Y. L. Li, H. Z. Fu

Research output: Contribution to journalArticlepeer-review

5 Scopus citations

Abstract

The effect of crystal orientation on the microstructure of a nickel-based crystalline superalloys during directional solidification was explored. Differently oriented crystals with [001] and [011] orientations were fabricated with seeding technique. The results showed that primary dendrite arm spacings decreased simultaneously with the increase of misroientation. The primary dendrites arrange in lines in [011] single crystal. For [001] oriented crystals, the size of γ' phase increased with the increasing of misorientation. However, it was observed that the size of γ decreased with large misorientation for [011] orientated growth. Meanwhile, more γ' in [011] crystals tended to be triangular.

Original languageEnglish
Pages (from-to)1291-1295
Number of pages5
JournalCrystal Research and Technology
Volume46
Issue number12
DOIs
StatePublished - Dec 2011

Keywords

  • crystal growth
  • crystal orientation
  • directional solidification
  • microstructure
  • superalloys

Fingerprint

Dive into the research topics of 'Effect of orientation on the microstructure of nickel-based crystalline superalloys'. Together they form a unique fingerprint.

Cite this