Effect factors on thermal and mechanical properties of SiO2 and TiB2 modified SiBCN-based adhesives

Xin'gang Luan; Min Li; Sen Chang; Yongguo Li; Kunjun Wang; Xuemei Song; Ralf Riedel; Laifei Cheng

doi:10.1016/j.ceramint.2020.04.286

Effect factors on thermal and mechanical properties of SiO₂ and TiB₂ modified SiBCN-based adhesives

Xin'gang Luan, Min Li, Sen Chang, Yongguo Li, Kunjun Wang, Xuemei Song, Ralf Riedel, Laifei Cheng

School of Materials Sience and Engineering

Research output: Contribution to journal › Article › peer-review

14 Scopus citations

Abstract

To further investigate the reinforcing factors on the adhesion strength of SiO₂ and TiB₂ modified SiBCN-based adhesives, the thermal stability analysis, microstructure observations and phase composition analysis were performed on four kinds of modified PSNB (Polyborosilazane) adhesives. With the different Si/B ratio and SiO₂ content, the room temperature adhesion strength reach up to 18.95, 12.04, 32.44 and 13.69 MPa for PPT-1, PPT-2, PPTS and PST respectively, after synthesized at 1000 °C in air. And then, the high temperature adhesion strength reach up to 12.3 and 16.4 MPa for PPT-1 and PPTS at 1000 °C in vacuum, respectively. Interestingly, it has been found that temperature, PSO, solid content and SiO₂ content all have a great influence on the adhesion performance of SiO₂ and TiB₂ modified SiBCN-based adhesives.

Original language	English
Pages (from-to)	19416-19424
Number of pages	9
Journal	Ceramics International
Volume	46
Issue number	11
DOIs	https://doi.org/10.1016/j.ceramint.2020.04.286
State	Published - 1 Aug 2020

Keywords

Adhesion strength
Si/B ratio
SiBCN-based ceramic
SiO content

Access to Document

10.1016/j.ceramint.2020.04.286

Cite this

@article{7cb2388b013a4e0484f99b28b9d2e741,

title = "Effect factors on thermal and mechanical properties of SiO2 and TiB2 modified SiBCN-based adhesives",

abstract = "To further investigate the reinforcing factors on the adhesion strength of SiO2 and TiB2 modified SiBCN-based adhesives, the thermal stability analysis, microstructure observations and phase composition analysis were performed on four kinds of modified PSNB (Polyborosilazane) adhesives. With the different Si/B ratio and SiO2 content, the room temperature adhesion strength reach up to 18.95, 12.04, 32.44 and 13.69 MPa for PPT-1, PPT-2, PPTS and PST respectively, after synthesized at 1000 °C in air. And then, the high temperature adhesion strength reach up to 12.3 and 16.4 MPa for PPT-1 and PPTS at 1000 °C in vacuum, respectively. Interestingly, it has been found that temperature, PSO, solid content and SiO2 content all have a great influence on the adhesion performance of SiO2 and TiB2 modified SiBCN-based adhesives.",

keywords = "Adhesion strength, Si/B ratio, SiBCN-based ceramic, SiO content",

author = "Xin'gang Luan and Min Li and Sen Chang and Yongguo Li and Kunjun Wang and Xuemei Song and Ralf Riedel and Laifei Cheng",

note = "Publisher Copyright: {\textcopyright} 2020 Elsevier Ltd and Techna Group S.r.l.",

year = "2020",

month = aug,

day = "1",

doi = "10.1016/j.ceramint.2020.04.286",

language = "英语",

volume = "46",

pages = "19416--19424",

journal = "Ceramics International",

issn = "0272-8842",

publisher = "Elsevier Ltd",

number = "11",

}

TY - JOUR

T1 - Effect factors on thermal and mechanical properties of SiO2 and TiB2 modified SiBCN-based adhesives

AU - Luan, Xin'gang

AU - Li, Min

AU - Chang, Sen

AU - Li, Yongguo

AU - Wang, Kunjun

AU - Song, Xuemei

AU - Riedel, Ralf

AU - Cheng, Laifei

PY - 2020/8/1

Y1 - 2020/8/1

N2 - To further investigate the reinforcing factors on the adhesion strength of SiO2 and TiB2 modified SiBCN-based adhesives, the thermal stability analysis, microstructure observations and phase composition analysis were performed on four kinds of modified PSNB (Polyborosilazane) adhesives. With the different Si/B ratio and SiO2 content, the room temperature adhesion strength reach up to 18.95, 12.04, 32.44 and 13.69 MPa for PPT-1, PPT-2, PPTS and PST respectively, after synthesized at 1000 °C in air. And then, the high temperature adhesion strength reach up to 12.3 and 16.4 MPa for PPT-1 and PPTS at 1000 °C in vacuum, respectively. Interestingly, it has been found that temperature, PSO, solid content and SiO2 content all have a great influence on the adhesion performance of SiO2 and TiB2 modified SiBCN-based adhesives.

AB - To further investigate the reinforcing factors on the adhesion strength of SiO2 and TiB2 modified SiBCN-based adhesives, the thermal stability analysis, microstructure observations and phase composition analysis were performed on four kinds of modified PSNB (Polyborosilazane) adhesives. With the different Si/B ratio and SiO2 content, the room temperature adhesion strength reach up to 18.95, 12.04, 32.44 and 13.69 MPa for PPT-1, PPT-2, PPTS and PST respectively, after synthesized at 1000 °C in air. And then, the high temperature adhesion strength reach up to 12.3 and 16.4 MPa for PPT-1 and PPTS at 1000 °C in vacuum, respectively. Interestingly, it has been found that temperature, PSO, solid content and SiO2 content all have a great influence on the adhesion performance of SiO2 and TiB2 modified SiBCN-based adhesives.

KW - Adhesion strength

KW - Si/B ratio

KW - SiBCN-based ceramic

KW - SiO content

UR - http://www.scopus.com/inward/record.url?scp=85084401377&partnerID=8YFLogxK

U2 - 10.1016/j.ceramint.2020.04.286

DO - 10.1016/j.ceramint.2020.04.286

M3 - 文章

AN - SCOPUS:85084401377

SN - 0272-8842

VL - 46

SP - 19416

EP - 19424

JO - Ceramics International

JF - Ceramics International

IS - 11

ER -

Effect factors on thermal and mechanical properties of SiO₂ and TiB₂ modified SiBCN-based adhesives

Abstract

Keywords

Access to Document

Other files and links

Fingerprint

Cite this