Attaining exceptional wear resistance in an in-situ ceramic phase reinforced NbMoWTa refractory high entropy alloy composite by Spark plasma sintering

The refractory high-entropy alloys (RHEAs) exhibit great potential as structural components for aerospace equipment. However, their lack of wear resistance and increased coefficient of friction at room temperature (RT) impose limitations on their practical applications. Therefore, further enhancements are required to improve their friction and wear properties under RT. In this context, the development of NbMoWTa(h-BN)_x RHEA ceramic composites in this work offers a viable solution to address this issue. Experimental results demonstrate that the addition of h-BN leads to the in-situ generation of (Nb,Ta)N/(Nb,Ta)₂N and (Nb,Ta)B₂ ceramic phases, significantly enhancing the hardness and wear resistance of the composites. The wear rate of NbMoWTa(h-BN)_0.5 reaching as low as 1.32 × 10⁻⁸ mm³/Nm, which is four orders of magnitude lower than that of the RHEA. The NbMoWTa RHEA exhibits significant adhesive wear, which can be effectively mitigated in composites through the uniform dispersion of ceramic phase particles with lower mean free path. The abrasive particles primarily interact with the hard strengthening phase, effectively inhibiting plastic deformation in their vicinity. Consequently, the reduced mean free path between the ceramic phases limits the likelihood of metal matrix removal. Subsequently, aided by the presence of ceramic phases, the spontaneous formation of protective third bodies further inhibit surface material removal and ultimately ensures exceptional wear resistance.