Ablation behavior and thermal protection performance of TaSi₂ coating for SiC coated carbon/carbon composites

For extending application of TaSi₂ in complex coating system, the ablation behavior and thermal protection performance of TaSi₂ coating is studied to evaluate its potential applications for anti-ablation protection of C/C composites. TaSi₂ coating is prepared by supersonic atmospheric plasma spraying (SAPS) on the surface of SiC coated carbon/carbon (C/C) composites. Phase variation and microstructure are characterized by XRD and SEM, respectively. During the ablation process, the coating is quickly oxidized to SiO₂ and Ta₂O₅ accompanied by a lot of heat consumption. The linear and mass ablation rates are 0.9 µm s⁻¹ and − 0.4 mg s⁻¹ after ablation for 80 s, respectively Results show that the prepared coating possesses optimal ablation performance under the heat flux of 2.4 MW/m². Moreover, the TaSi₂ coating and SiC inner coating have good chemical and physical compatibility during the ablation process. Therefore, the excellent performance of TaSi₂ coating during the ablation process makes it a candidate for anti-ablation protection for C/C composites.