T1 - 3DN C/SiC composites with different porosities for tunable lubrication performance
AU - Yang, Yubo
AU - Zhao, Yu
AU - Mei, Hui
AU - Chen, Chao
AU - Cheng, Laifei
N1 - Publisher Copyright:
© 2021 Elsevier Ltd and Techna Group S.r.l.
PY - 2021/5/15
Y1 - 2021/5/15
N2 - Three-dimensional needled carbon fiber reinforced silicon carbide (3DN C/SiC) composites are potential candidates for lubrication systems because of their great lubrication and wear resistance performance. In this paper, different thicknesses of SiC were deposited by chemical vapor infiltration (CVI) method to prepare 3DN C/SiC composites with controllable porosities, aiming to investigate the effect of different porosities on their lubrication performance under the various load-bearing conditions. Results showed that the friction coefficients of 3DN C/SiC composites decreased with increasing porosity, and the wear rate of the sample with a porosity of 60% was much higher than that of samples with porosity of 30% and 15%. Specifically, the 3DN C/SiC sample with a porosity of 30% exhibited ideal lubricating performance under the load of 10 N, with a lowest friction coefficient of 0.230 and favorable wear rate of 2.20 × 10−4 mm3/(N·m). As for the effect of load, the friction coefficient and wear rate of the sample with a porosity of 30% decreased with increasing load. The lubrication mechanism is mainly the formation of friction film. Therefore, this study presented an effective way to enhance the lubrication performance of 3DN C/SiC composites, which makes it practically applicable in lubrication systems.
AB - Three-dimensional needled carbon fiber reinforced silicon carbide (3DN C/SiC) composites are potential candidates for lubrication systems because of their great lubrication and wear resistance performance. In this paper, different thicknesses of SiC were deposited by chemical vapor infiltration (CVI) method to prepare 3DN C/SiC composites with controllable porosities, aiming to investigate the effect of different porosities on their lubrication performance under the various load-bearing conditions. Results showed that the friction coefficients of 3DN C/SiC composites decreased with increasing porosity, and the wear rate of the sample with a porosity of 60% was much higher than that of samples with porosity of 30% and 15%. Specifically, the 3DN C/SiC sample with a porosity of 30% exhibited ideal lubricating performance under the load of 10 N, with a lowest friction coefficient of 0.230 and favorable wear rate of 2.20 × 10−4 mm3/(N·m). As for the effect of load, the friction coefficient and wear rate of the sample with a porosity of 30% decreased with increasing load. The lubrication mechanism is mainly the formation of friction film. Therefore, this study presented an effective way to enhance the lubrication performance of 3DN C/SiC composites, which makes it practically applicable in lubrication systems.
KW - 3DN C/SiC composites
KW - Friction film
KW - Lubrication performance
KW - Porosity
UR - http://www.scopus.com/inward/record.url?scp=85100371620&partnerID=8YFLogxK
U2 - 10.1016/j.ceramint.2021.01.263
DO - 10.1016/j.ceramint.2021.01.263
M3 - 文章
AN - SCOPUS:85100371620
SN - 0272-8842
VL - 47
SP - 13948
EP - 13956
JO - Ceramics International
JF - Ceramics International
IS - 10
ER -