分散剂反应直接凝固注模成型制备碳化硅陶瓷

Translated title of the contribution: Direct Coagulation Casting of Silicon Carbide Ceramics via Dispersant Reaction

Ke Gan, Jie Xu, Zheng Wang, Yuju Lu, Yali Wang, Jinlong Yang

Research output: Contribution to journalArticlepeer-review

Abstract

Direct coagulation casting via dispersant reaction is a novel colloidal forming method for ceramics. The well disperse silicon carbide suspension can be coagulated in-situ by DCC via dispersant reaction. Silicon carbide suspension was prepared using surface chemical treatment powder. Ammonium carbonate ((NH4)2CO3) was used to leach the silicon carbide powder. Tetramethyl ammonium hydroxide (TMAH) with content of 0.2 wt% was used as dispersant. 2 vol% glycerol diacetate (GDA) was added as coagulation agent. Tetramethyl ammonium hydroxide reacted with acetic acid which hydrolyzed from glycerol diacetate at elevated temperature, and then desorbed from silicon carbide particles. Zeta potential of suspension decreased due to desorption of dispersant, and the suspension coagulated in-suit from the instability of the silicon carbide particle. The silicon carbide green body with compressive strength of 1.13 MPa was coagulated at 70 °C. The silicon carbide ceramic with flexural strength of 697 MPa was pressureless sintered at 1950 °C for 2 h under 0.1 MPa argon atmosphere.

Translated title of the contributionDirect Coagulation Casting of Silicon Carbide Ceramics via Dispersant Reaction
Original languageChinese (Traditional)
Pages (from-to)22-26
Number of pages5
JournalXiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering
Volume47
StatePublished - 1 Jul 2018

Fingerprint

Dive into the research topics of 'Direct Coagulation Casting of Silicon Carbide Ceramics via Dispersant Reaction'. Together they form a unique fingerprint.

Cite this