Thermal stability of iridium coating prepared by MOCVD

Wenbin Yang; Litong Zhang; Yunfeng Hua; Laifei Cheng

doi:10.1016/j.ijrmhm.2008.02.001

Thermal stability of iridium coating prepared by MOCVD

Wenbin Yang
, Litong Zhang
, Yunfeng Hua
, Laifei Cheng

材料学院

Northwestern Polytechnical University Xian

科研成果: 期刊稿件 › 文章 › 同行评审

38 引用（Scopus）

摘要

A multilayer Ir coating with equiaxed grains was prepared using metalorganic chemical vapor deposition on Nb substrates by thermal decomposition of Ir(acac)₃ precursor. Thermal stability of the coating was investigated at 1200 °C and 1300 °C in Ar. The Ir coating exhibited different thermal stabilities depending on heating temperatures. After heat treatment, the prepared nanometer and sub-micrometer grains grow obviously and grain size increased with rising heating temperature. Pores diffused outward and their amount reduced. After heat treatment, the coating gradually transformed into a compact layer. Nb diffused into Ir coating during heat treatment, and solid solutions were formed at 1300 °C.

源语言	英语
页（从-至）	33-36
页数	4
期刊	International Journal of Refractory Metals and Hard Materials
卷	27
期	1
DOI	https://doi.org/10.1016/j.ijrmhm.2008.02.001
出版状态	已出版 - 1月 2009

访问文件

10.1016/j.ijrmhm.2008.02.001

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{62072d73c4844183a3b94edf03d78446,

title = "Thermal stability of iridium coating prepared by MOCVD",

abstract = "A multilayer Ir coating with equiaxed grains was prepared using metalorganic chemical vapor deposition on Nb substrates by thermal decomposition of Ir(acac)3 precursor. Thermal stability of the coating was investigated at 1200 °C and 1300 °C in Ar. The Ir coating exhibited different thermal stabilities depending on heating temperatures. After heat treatment, the prepared nanometer and sub-micrometer grains grow obviously and grain size increased with rising heating temperature. Pores diffused outward and their amount reduced. After heat treatment, the coating gradually transformed into a compact layer. Nb diffused into Ir coating during heat treatment, and solid solutions were formed at 1300 °C.",

keywords = "Diffusion, Ir coating, MOCVD, Multilayer structure, Nb, Thermal stability",

author = "Wenbin Yang and Litong Zhang and Yunfeng Hua and Laifei Cheng",

year = "2009",

month = jan,

doi = "10.1016/j.ijrmhm.2008.02.001",

language = "英语",

volume = "27",

pages = "33--36",

journal = "International Journal of Refractory Metals and Hard Materials",

issn = "0263-4368",

publisher = "Elsevier B.V.",

number = "1",

}

TY - JOUR

T1 - Thermal stability of iridium coating prepared by MOCVD

AU - Yang, Wenbin

AU - Zhang, Litong

AU - Hua, Yunfeng

AU - Cheng, Laifei

PY - 2009/1

Y1 - 2009/1

N2 - A multilayer Ir coating with equiaxed grains was prepared using metalorganic chemical vapor deposition on Nb substrates by thermal decomposition of Ir(acac)3 precursor. Thermal stability of the coating was investigated at 1200 °C and 1300 °C in Ar. The Ir coating exhibited different thermal stabilities depending on heating temperatures. After heat treatment, the prepared nanometer and sub-micrometer grains grow obviously and grain size increased with rising heating temperature. Pores diffused outward and their amount reduced. After heat treatment, the coating gradually transformed into a compact layer. Nb diffused into Ir coating during heat treatment, and solid solutions were formed at 1300 °C.

AB - A multilayer Ir coating with equiaxed grains was prepared using metalorganic chemical vapor deposition on Nb substrates by thermal decomposition of Ir(acac)3 precursor. Thermal stability of the coating was investigated at 1200 °C and 1300 °C in Ar. The Ir coating exhibited different thermal stabilities depending on heating temperatures. After heat treatment, the prepared nanometer and sub-micrometer grains grow obviously and grain size increased with rising heating temperature. Pores diffused outward and their amount reduced. After heat treatment, the coating gradually transformed into a compact layer. Nb diffused into Ir coating during heat treatment, and solid solutions were formed at 1300 °C.

KW - Diffusion

KW - Ir coating

KW - MOCVD

KW - Multilayer structure

KW - Nb

KW - Thermal stability

UR - https://www.scopus.com/pages/publications/53549130237

U2 - 10.1016/j.ijrmhm.2008.02.001

DO - 10.1016/j.ijrmhm.2008.02.001

M3 - 文章

AN - SCOPUS:53549130237

SN - 0263-4368

VL - 27

SP - 33

EP - 36

JO - International Journal of Refractory Metals and Hard Materials

JF - International Journal of Refractory Metals and Hard Materials

IS - 1

ER -

Thermal stability of iridium coating prepared by MOCVD

摘要

访问文件

其它文件与链接

指纹

引用此