Ternary eutectic growth of Ag-Cu-Sb alloy within ultrasonic field

The liquid to solid transformation of ternary Ag_42.4Cu _21.6Sb₃₆ eutectic alloy was accomplished in an ultrasonic field with a frequency of 35 kHz, and the growth mechanism of this ternary eutectic was examined. Theoretical calculations predict that the sound intensity in the liquid phase at the solidification interface increases gradually as the interface moves up from the sample bottom to its top. The growth mode of (ε + θ + Sb) ternary eutectic exhibits a transition of "divorced eutectic-mixture of anomalous and regular structures-regular eutectic" along the sample axis due to the inhomogeneity of sound field distribution. In the top zone with the highest sound intensity, the cavitation effect promotes the three eutectic phases to nucleate independently, while the acoustic streaming efficiently suppresses the coupled growth of eutectic phases. In the meantime, the ultrasonic field accelerates the solute transportation at the solid-liquid interface, which reduces the solute solubility of eutectic phases.