Surface Analyses of High-Temperature Oxidated TiAl-Based Alloys

Henglei Qu; Lian Zhou; Hairong Wei

Surface Analyses of High-Temperature Oxidated TiAl-Based Alloys

Henglei Qu
, Lian Zhou
, Hairong Wei

Northwest Institute for Nonferrous Metal Research
Northeastern University China

科研成果: 期刊稿件 › 文章 › 同行评审

6 引用（Scopus）

摘要

Five TiAl-based alloys (Ti-50Al, Ti-48Al, Ti-52Al, Ti-48Al-1Cr, Ti-48Al-4Cr) oxidized interruptedly at 700°C∼1 000°C for 100 h in static air. The surface morphologies, phase constitutions and particle distributions of the oxide films formed on the alloys were observed and analyzed using SEM/EDS and XRD techniques. The results show that the oxidation products mainly consist of R -TiO₂ and α -Al₂O₃. The oxides exist in mixture state when the alloys oxidized at low temperature for short time, while a pillar-like rutile layer forms on the porous mixture oxide when the alloys oxidized at high temperature for long time.

源语言	英语
页（从-至）	90-93
页数	4
期刊	Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering
卷	29
期	2
出版状态	已出版 - 4月 2000
已对外发布	是

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{9eed5096e5af439ca1e6f4b874e4943c,

title = "Surface Analyses of High-Temperature Oxidated TiAl-Based Alloys",

abstract = "Five TiAl-based alloys (Ti-50Al, Ti-48Al, Ti-52Al, Ti-48Al-1Cr, Ti-48Al-4Cr) oxidized interruptedly at 700°C∼1 000°C for 100 h in static air. The surface morphologies, phase constitutions and particle distributions of the oxide films formed on the alloys were observed and analyzed using SEM/EDS and XRD techniques. The results show that the oxidation products mainly consist of R -TiO2 and α -Al2O3. The oxides exist in mixture state when the alloys oxidized at low temperature for short time, while a pillar-like rutile layer forms on the porous mixture oxide when the alloys oxidized at high temperature for long time.",

keywords = "High temperature oxidation, Surface analysis, TiAl",

author = "Henglei Qu and Lian Zhou and Hairong Wei",

year = "2000",

month = apr,

language = "英语",

volume = "29",

pages = "90--93",

journal = "Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering",

issn = "1002-185X",

publisher = "Science Press ",

number = "2",

}

TY - JOUR

T1 - Surface Analyses of High-Temperature Oxidated TiAl-Based Alloys

AU - Qu, Henglei

AU - Zhou, Lian

AU - Wei, Hairong

PY - 2000/4

Y1 - 2000/4

N2 - Five TiAl-based alloys (Ti-50Al, Ti-48Al, Ti-52Al, Ti-48Al-1Cr, Ti-48Al-4Cr) oxidized interruptedly at 700°C∼1 000°C for 100 h in static air. The surface morphologies, phase constitutions and particle distributions of the oxide films formed on the alloys were observed and analyzed using SEM/EDS and XRD techniques. The results show that the oxidation products mainly consist of R -TiO2 and α -Al2O3. The oxides exist in mixture state when the alloys oxidized at low temperature for short time, while a pillar-like rutile layer forms on the porous mixture oxide when the alloys oxidized at high temperature for long time.

AB - Five TiAl-based alloys (Ti-50Al, Ti-48Al, Ti-52Al, Ti-48Al-1Cr, Ti-48Al-4Cr) oxidized interruptedly at 700°C∼1 000°C for 100 h in static air. The surface morphologies, phase constitutions and particle distributions of the oxide films formed on the alloys were observed and analyzed using SEM/EDS and XRD techniques. The results show that the oxidation products mainly consist of R -TiO2 and α -Al2O3. The oxides exist in mixture state when the alloys oxidized at low temperature for short time, while a pillar-like rutile layer forms on the porous mixture oxide when the alloys oxidized at high temperature for long time.

KW - High temperature oxidation

KW - Surface analysis

KW - TiAl

UR - https://www.scopus.com/pages/publications/0346930458

M3 - 文章

AN - SCOPUS:0346930458

SN - 1002-185X

VL - 29

SP - 90

EP - 93

JO - Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering

JF - Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering

IS - 2

ER -

Surface Analyses of High-Temperature Oxidated TiAl-Based Alloys

摘要

其它文件与链接

学术指纹

引用此