Structure and oxidation behavior of a plasma sprayed yttrium silicates coated SiC-C/C with a glass outer sealant from 1 573K to 1 873K

Different compositions of yttrium silicates coatings were deposited on SiC-C/C by plasma spraying and an outer borosilicate glass was applied on the yttrium silicates coatings surfaces. The structure of the multi-layer coatings was characterized by XRD and SEM analyses. High temperature oxidation behavior of the multi-layer coatings coated C/C composites was investigated. Results show that SiC/2SiO₂•Y₂O₃/1.5SiO ₂•Y₂O₃/ SiO₂•Y ₂O₃/glass multi-layer coating has better high temperature oxidation resistance, protecting carbon/ carbon composites from oxidation at 1 773 K in air for 164 h with the weight loss of 1.65%. The oxidation weight loss of the coated C/C with time accorded with parabolic rule in the temperature range 1 573 K-1 873 K; and the corresponding oxidation activation energy of the coated carbon/carbon composites is 132.2 kJ/mol.